1.Speck counts:≤10/0/SH/T 1541-2006
2.Melt Flow Index(MFR) g/10min: 0.30~0.40/0.35/GB/T 3682-2000
3.Density (23℃) kg/m³: 953.5~956.5/955.5/GB/T 1033.2-2010
4.Ash Wt%: ≤0.1/0.04/CPC-IVGFTIR
5.Color:≥180/310/CPC-IVD
6.Tensile yield stress MPa :≥26/28.6/ASTM D638-2010
7.Tensile break strain %:≥500/787/ASTM D638-2010
8.ESCR condition B, F50:≥25/66/GB/T 1842-2008
1.Speck counts:≤10/0/SH/T 1541-2006
2.Melt Flow Index(MFR) g/10min: 0.30~0.40/0.35/GB/T 3682-2000
3.Density (23℃) kg/m³: 953.5~956.5/955.5/GB/T 1033.2-2010
4.Ash Wt%: ≤0.1/0.04/CPC-IVGFTIR
5.Color:≥180/310/CPC-IVD
6.Tensile yield stress MPa :≥26/28.6/ASTM D638-2010
7.Tensile break strain %:≥500/787/ASTM D638-2010
8.ESCR condition B, F50:≥25/66/GB/T 1842-2008
1.Speck counts:≤10/0/SH/T 1541-2006
2.Melt Flow Index(MFR) g/10min: 0.30~0.40/0.35/GB/T 3682-2000
3.Density (23℃) kg/m³: 953.5~956.5/955.5/GB/T 1033.2-2010
4.Ash Wt%: ≤0.1/0.04/CPC-IVGFTIR
5.Color:≥180/310/CPC-IVD
6.Tensile yield stress MPa :≥26/28.6/ASTM D638-2010
7.Tensile break strain %:≥500/787/ASTM D638-2010
8.ESCR condition B, F50:≥25/66/GB/T 1842-2008
1.Speck counts:≤10/0/SH/T 1541-2006
2.Melt Flow Index(MFR) g/10min: 0.30~0.40/0.35/GB/T 3682-2000
3.Density (23℃) kg/m³: 953.5~956.5/955.5/GB/T 1033.2-2010
4.Ash Wt%: ≤0.1/0.04/CPC-IVGFTIR
5.Color:≥180/310/CPC-IVD
6.Tensile yield stress MPa :≥26/28.6/ASTM D638-2010
7.Tensile break strain %:≥500/787/ASTM D638-2010
8.ESCR condition B, F50:≥25/66/GB/T 1842-2008
1.Speck counts:≤10/0/SH/T 1541-2006
2.Melt Flow Index(MFR) g/10min: 0.30~0.40/0.35/GB/T 3682-2000
3.Density (23℃) kg/m³: 953.5~956.5/955.5/GB/T 1033.2-2010
4.Ash Wt%: ≤0.1/0.04/CPC-IVGFTIR
5.Color:≥180/310/CPC-IVD
6.Tensile yield stress MPa :≥26/28.6/ASTM D638-2010
7.Tensile break strain %:≥500/787/ASTM D638-2010
8.ESCR condition B, F50:≥25/66/GB/T 1842-2008
Prev:HD5502S
Next:Period